Frameless honeycomb panel
It adopts high-quality aluminum plate laminated with high-density honeycomb core technology. The structure adopts natural folding technology and natural seam splicing to achieve true micro-seam technology.
The surface coating is imported titanium dioxide, which has high stability, high hiding power, high durability, yellowing resistance, stable color matching, ultraviolet shielding, and high efficiency and scrub resistance.
The glossiness is ≤7° (close to latex paint), the texture is delicate, and the visual effect is elegant and soft.
Sound insulation, heat insulation and impact resistance, the overall density of 10mm is more scientific. After repeated testing by the R&D team, the thickness of 10mm without the aid of a frame has excellent sound insulation and
It has the best effect in terms of heat insulation and impact resistance, better flatness, and can also greatly improve space utilization.
Inorganic Core Material Is Green And Environmentally Friendly
Good Fire Prevention And Fire Safety Performance
Installation Is Fast And Very Smooth And Clean
Lightweight Sound Insulation And Heat Insulation
| Test items | Standard requirement | Test results | Single conclusion | Testing base | |
| Surface hardness | ≥HB | 2H (Zhonghua brand pencil) | Conform to | JC/T 2113-2012 7.7.1 | |
| GB/T 6739-2006 | |||||
| Adhesion | Standard laboratory conditions | Level 0 | Level 0 | Conform to | Q/CYCTC 0110-2017 |
| GB/T 17748-2008 7.7.4 | |||||
| GB/T 9286-1998(2004) | |||||
| Hydrochloric acid resistance | No change | No change | Conform to | Q/CYCTC 0110-2017 | |
| GB/T 17748-2008 7.7.7 | |||||
| Alkali resistance | No change | No change | Conform to | Q/CYCTC 0110-2017 | |
| GB/T 17748-2008 7.7.8 | |||||
| GB/T 11942-1989 | |||||
| Flat tensile strength | Average value≥0.6Mpa; Minimum value≥0.4Mpa | Average 1.13Mpa | Conform to | JC/T 2113-2012 7.7.13 | |
| Minimum value 0.97Mpa | GB/T 1452-2005 | ||||
| Flat compressive strength | ≥0.6Mpa | 1.07Mpa | Conform to | JC/T 2113-2012 7.7.13 | |
| Flat compression elastic modulus | ≥25Mpa | 45.3Mpa | Conform to | GB/T 1455-2005 | |
| Plane shear strength | ≥0.4Mpa | 0.54Mpa | Conform to | JC/T 2113-2012 7.7.14 | |
| Plane shear elastic modulus | ≥3.0Mpa | 3.73Mpa | Conform to | GB/T 1455-2005 | |
| Shear stiffness | ≥1.0x104N | 3.53x104N | Conform to | JC/T 2113-2012 7.7.15 | |
| GB/T 1456-2005 | |||||
| Formaldehyde release (dryer method) | / | Not detected (<0.10mg/L) | / | GB/T 17657-2013 4.59 | |
Frameless honeycomb panel Rendering
Frameless honeycomb panel Rendering
Frameless honeycomb panel Rendering
Ten year ultra long waterproof lifespan and 97% recycling rate
Reduce carbon emissions by over 40% compared to traditional buildings
External noise level of 90 decibels can be reduced to below 40 decibels inside the cabin
Night sleep quality satisfaction increased by 52%, repurchase rate increased by 35%
Design
Further design of overseas project drawings
Customization
Product supply and customization
Logistic
Logistics and overseas customs clearance
Cultivate
Product training
Construction
Local construction delivery installation training
After-Sales
After-sales service guarantee